Recrystallization Anneal

 

Abstract: Recrystallization annealing is a heat treating process used to modify the properties of cold-worked metal.  This article discusses the reasons for preforming a recrystallization anneal, the metallurgical changes that take place within a metal during cold working and annealing, the effects of these metallurgical changes on the properties of metals, and the effects of annealing temperature and time on the final microstructure and properties of annealed metals.

Many metal fabrication processes involve cold-working, such as cold rolling sheet and plate, wire drawing, and deep drawing.  Due to metallurgical changes that occur to a metal during cold working, the ductility of a metal decreases as the amount of cold-working increases.  There comes a point when additional cold working is not possible without causing the metal to crack.  At this point, it is necessary to anneal the metal if continued cold-working is required.

See metallurgy courses & webinars
Need help with your product?

The specific annealing process used is called recrystallization anneal.  During this annealing process, metallurgical changes occur that returns the metal to its pre-cold-worked state.  These changes result in a reduction of the metal’s yield and tensile strength and an increase in its ductility, enabling further cold working.  In order for these changes to occur, the metal must be heated above its recrystallization temperature.  The recrystallization temperature for a particular metal depends on its composition.

Metallurgical effects of cold working

During cold-working there is an increase in the number of dislocations in a metal compared to its pre-cold-worked condition.  Dislocations are defects in the arrangement of atoms in a metal (discussed in Principles of Metallurgy).  The increase in the number of dislocations causes a metal’s yield and tensile strength to increase and its ductility to decrease.  After a certain amount of cold work, a metal cannot be cold worked further without cracking.  The amount of cold working that a particular metal can withstand before cracking depends on its composition and microstructure.

Metallurgical effects of recrystallization anneal

During a recrystallization anneal, new grains form in a cold-worked metal.  These new grains have a greatly reduced number of dislocations compared to the cold-worked metal.  This change returns the metal to its pre-cold-worked state, with lower strength and increased ductility.

With continued time at the annealing temperature, some of the newly formed grains grow at the expense of neighboring grains.  There is some further decrease in strength and increase in ductility as the average grain size increases during the grain growth phase of the annealing process.

The final grain size depends on the annealing temperature and annealing time.  For a particular annealing temperature, as the time at the temperature increases the grain size increases.  For a particular annealing time, as the temperature increases the grain size increases.  A piece of metal with large grains has lower strength and more ductility than a piece of metal of the same alloy with smaller grains.

The figure shows micrographs of a brass alloy that was cold-rolled to 50% of its original thickness and annealed at two different temperatures.  The figure on the left shows the microstructure of the cold rolled sample.  The center figure shows the microstructure of a sample that was cold rolled and then annealed at 1022 °F (550 °C) for 1 hour.  The figure on the right shows the microstructure of a sample that was cold rolled and then annealed at 1202 °F (650 °C) for 1 hour.

Annealed brass grains

The cold-rolled sample had a yield strength of 80 ksi (550 MPa).  The sample that was annealed at 1022 °F (550 °C) for 1 hour had yield strength of 11 ksi (75 MPa).  Many small grains are present in this sample.  The sample that was annealed at 1202 °F (650 °C) for 1 hour had yield strength of 9 ksi (60 MPa).  Fewer, large grains were present in this sample compared to the center sample.

See metallurgy courses & webinars
Need help with your product?

Other reason for recrystallization anneal

In addition to enabling additional cold-working, recrystallization annealing is also used as a final processing step to produce metal sheet, plate, wire, or bar with specific mechanical properties.  Control of the annealing temperature and time, heating rate up to the annealing temperature, and amount of cold-working prior to anneal is important for obtaining the desired grain size, and therefore the desired mechanical properties.

  • "A group of us took several courses (Principles of Metallurgy, Metallurgy of Steel, Corrosion of Metals) to become more knowledgeable about the science of metals to avoid problems. For me, the biggest impact of the training was on working with suppliers. I feel more confident asking questions and I now know the suppliers which know their stuff and which ones don’t. And it was great being able to get the training when it was convenient for me."

    Sam Bloodgood, VP Process Improvement, Hydraforce, Inc.
  • "I oversee several operations, including steel heat treating and laser welding. However, my background was in the construction materials industry. Principles of Metallurgy gave me the knowledge to have meaningful discussions with my engineers and be able to ask them better questions."

    Tom Parkman, Plant Manager, Simonds International.
  • “Principles of Metallurgy exceeded my expectations. The content was straightforward enough not to be burdensome, yet deep enough to provide a practical review of fundamental principles. I recommend this course to any engineer or technical person who has been out of school and working in industry for several years, but not necessarily having been focused on metallurgy.”

    Andy Jacobs, Staff Engineer, DePuy Orthopaedics, Inc.
  • “The Principles of Metallurgy course is broke up into convenient length modules that can be fit into the busiest schedule. The course is a good review for engineers who had a materials class ten or more years ago.”

    Paul Flury B/E Aerospace
  • “This is an excellent course (Metallurgy of Steel Heat Treating) for learning basic heat treating practices. The course introduces and covers a broad range of processes. I would recommend it for anyone in the steel business.”

    Jim Marks, Magellan Corporation
  • “This course has given me more confidence in my job and given me a better understanding of some of the heat treatments used in the business.”

    Mark Winter, Abbey Forged Products

Have more questions? Email mpfeifer@imetllc.com or call 847.528.3467

Why Industrial Metallurgists?

  • Practical, up-to-date content.
  • Metallurgy expertise and 20+ years of experience.
  • Courses designed for non-metallurgists.
  • Training accessible from anywhere with internet access.
  • Engaging content.
  • Convenience. Learn when it suits your schedule.
  • Avoid being overwhelmed with too much information at one time. Set your own pace.