Introduction to Stainless Steel

 

Stainless steels are steels with a minimum of 10% chromium. They gain their resistance to corrosion from a thin, tenacious surface layer of chromium oxide. If the oxide layer is physically damaged there is rapid regeneration of the layer, thus preserving the corrosion resistance. However, a chemical environment that can disrupt this layer can initiate corrosion. Consequently, stainless steel is highly resistant to atmospheric corrosion, but not immune to corrosion in all environments.

Stainless steels fall into several general classes: austenitic, ferritic, martensitic, duplex, and precipitation hardened. The distinction between each class is based primarily on the predominant phase present in the stainless steel as determined by the major alloying elements.

See metallurgy courses & webinars
Need help with your product?

The major alloying elements in stainless steels are chromium and nickel. Chromium primarily provides corrosion resistance and additional strength. Nickel provides strength and some corrosion resistance. Minor alloying elements include manganese, carbon, and molybdenum. Manganese is present in steels in small quantities, but at higher concentrations it stabilizes austenite and partially replaces nickel in the 200-series steels. Carbon is largely an impurity in austenitic steel, but it is a strengthening element in ferritic and martensitic steel, much as it is for carbon and low-alloy steel. Molybdenum provides additional strength and resistance to chloride pitting. Other elements, such as titanium or niobium, serve other purposes specific to the application for which the alloy was developed.

400-series steels were the first versions of stainless steel. They include the ferritic and martensitic grades that contain only chromium as a major alloying element, making them less expensive than austenitic grades. They are magnetic, generally more resistant to chloride attack than 300-series alloys, and some grades may be strengthened by heat treating.

Type 410 contains about 12% chromium. The ability to strengthen this alloy by heat treating to form martensite makes it a martensitic grade. Its low chromium content provides modest corrosion resistance. Given enough time, exposure to weather will cause it to rust. Type 430 is a ferritic grade that contains about 17% chromium. It cannot be strengthened by heat treating. 400-series stainless steels are generally more resistant to chloride attack than 300-series.

With sufficient quantities of nickel, stainless steel remains austenite at room temperature, creating the austenitic steels. They are nonmagnetic and cannot be heat treated for through hardening like carbon steels because the phase transformation to martensite does not occur in these alloys. The primary reason for their use is their superior resistance to corrosion in the atmosphere and aggressive chemical environments compared to 400-series.

300-series alloys contain chromium and nickel, and are the most popular austenitic grades. Types 301 and 304 are the most common alloys in use and are for general use. They contain 18% chromium, 9% to 10% nickel, and up to 0.15% carbon (301) or 0.08% carbon (304) as an impurity. Other 300-series alloys are modified versions of these alloys to achieve specific properties. Type 316 contains 2%-3% molybdenum to improve the resistance to corrosion in chloride-containing environments. Types 304L, 316L and other L-grades contain reduced carbon, less than 0.03%, to avoid microstructure changes during welding and other thermal processes which can damage the corrosion resistance. This detrimental change is known as sensitization. Types 321 and 347 contain small amounts of titanium and niobium, respectively, to prevent sensitization. They are capable of service at elevated temperatures, while the L-grades are intended to resist sensitization during fabrication. The image below shows the austenite grains in a 304 alloy.

StainlessFigure1

Austenite grains in a 304 alloy. The particles on the grain boundaries are chromium carbides.

200-series steels, also austenitic, have manganese substituted for some of the nickel as a cost-saving measure. Grade 201 contains about 17% chromium, 6.5% manganese, and 4% nickel. It has corrosion resistance similar to 301.

Precipitation hardening (PH) steels are strengthened by heat treating to form precipitates, as well as by martensite formation. They can be strengthened to higher hardness than 400-series grades by an aging method similar to that of aluminum alloys. 17-4 PH and 17-7 PH steels contain 17% chromium and 4% or 7% nickel, respectively. Minor alloying elements can include copper, titanium and niobium, and others.

See metallurgy courses & webinars
Need help with a failure analysis?

Duplex stainless steels allow savings in material costs in corrosive applications such as chemical processing, including chloride- and sulfur-bearing environments. They consist of a mixture of austenite and ferrite in roughly equal proportions. Duplex stainless steels are subdivided into lean, standard, super, or hyper duplex based on the quantity of alloying elements. Duplex stainless steels contain more chromium and less nickel than 300-series and typically include nitrogen as an additional austenite stabilizer and molybdenum for corrosion resistance. 2205 (22% chromium, 5% nickel, and 3% molybdenum) is a common standard duplex stainless steel, and 2507 (25% Cr, 7% Ni plus 4% Mo) is a common super-duplex steel. The micrograph below shows a duplex stainless steel.

StainlessFigure2

Micrograph of a duplex stainless steel. The brown colored phase is ferrite and the light colored phase is austenite. (Courtesy of Charles Young, P.E.)

The broad array of stainless steels available provides a vast portfolio of capabilities. However, each alloy has distinct advantages and disadvantages. When selecting a grade of stainless steels available it is important to consider how components will be fabricated and joined together, the specific environment to which it will be exposed, in addition to the considerations common to other alloys such as mechanical requirements and cost.

More information about stainless steels is in ASM Specialty Handbook: Stainless Steels by J.R. Davis and ASM Metals Handbook Volume 1: Properties and Selection of Irons, Steels, and High-Performance Alloys. This article was written with the assistance of Charles Young, P.E.

  • "A group of us took several courses (Principles of Metallurgy, Metallurgy of Steel, Corrosion of Metals) to become more knowledgeable about the science of metals to avoid problems. For me, the biggest impact of the training was on working with suppliers. I feel more confident asking questions and I now know the suppliers which know their stuff and which ones don’t. And it was great being able to get the training when it was convenient for me."

    Sam Bloodgood, VP Process Improvement, Hydraforce, Inc.
  • "I oversee several operations, including steel heat treating and laser welding. However, my background was in the construction materials industry. Principles of Metallurgy gave me the knowledge to have meaningful discussions with my engineers and be able to ask them better questions."

    Tom Parkman, Plant Manager, Simonds International.
  • “Principles of Metallurgy exceeded my expectations. The content was straightforward enough not to be burdensome, yet deep enough to provide a practical review of fundamental principles. I recommend this course to any engineer or technical person who has been out of school and working in industry for several years, but not necessarily having been focused on metallurgy.”

    Andy Jacobs, Staff Engineer, DePuy Orthopaedics, Inc.
  • “The Principles of Metallurgy course is broke up into convenient length modules that can be fit into the busiest schedule. The course is a good review for engineers who had a materials class ten or more years ago.”

    Paul Flury B/E Aerospace
  • “This is an excellent course (Metallurgy of Steel Heat Treating) for learning basic heat treating practices. The course introduces and covers a broad range of processes. I would recommend it for anyone in the steel business.”

    Jim Marks, Magellan Corporation
  • “This course has given me more confidence in my job and given me a better understanding of some of the heat treatments used in the business.”

    Mark Winter, Abbey Forged Products

Have more questions? Email mpfeifer@imetllc.com or call 847.528.3467

Why Industrial Metallurgists?

  • Practical, up-to-date content.
  • Metallurgy expertise and 20+ years of experience.
  • Courses designed for non-metallurgists.
  • Training accessible from anywhere with internet access.
  • Engaging content.
  • Convenience. Learn when it suits your schedule.
  • Avoid being overwhelmed with too much information at one time. Set your own pace.